Method of curing an anisotropic conductive compound

ABSTRACT

Conductive material or particles of an anisotropic conductive compound or material sandwiched between at least two aligned conductive contacts are vibrated mechanically, magnetically, or both mechanically and magnetically while the anisotropic conductive compound is curing. The conductive material is subjected to a static, substantially homogeneous DC magnetic field (i) before, (ii) following or (iii) at least partially during the time the conductive material is being vibrated.

CROSS REFERENCE TO RELATED APPLICATION

[0001] This application is a continuation-in-part of U.S. application Ser. No. 10/205,515. filed Jul. 25, 2002.

BACKGROUND OF THE INVENTION

[0002] 1. Field of the Invention

[0003] The present invention relates to an anisotropic conductive compound or material and a method of curing thereof.

[0004] 2. Description of Related Art

[0005] Anisotropic conductive compounds are utilized to form conductive paths between pairs of aligned contacts, such as a contact on an integrated circuit or integrated circuit package and a contact of a printed circuit board. A typical anisotropic conductive compound includes conductive particles suspended in a binder. Such anisotropic conductive compound can be interposed in an uncured state between the integrated circuit or integrated circuit package and the substrate whereafter the anisotropic conductive compound can be cured to form conductive paths between contacts on the integrated circuit or integrated circuit package and the substrate while, at the same time, bonding the integrated circuit or integrated circuit package to the substrate.

[0006] Heretofore, anisotropic conductive compounds of the type described above were formed into a film which was interposed between the integrated circuit or integrated package and the substrate whereupon, with the application of pressure between the integrated circuit or integrated circuit package and the substrate in the presence of a curing heat, the conductive paths between aligned contacts of the integrated circuit or integrated circuit package and substrate, and the bonding of the integrated circuit or integrated circuit package to the substrate occurs.

[0007] A problem with prior art anisotropic conductive compounds is that they require the use of pressure and curing heat in order to form the conductive paths at the same time the bond is formed between the integrated circuit or integrated circuit package and the substrate. Another problem is that the film form of the prior art anisotropic conductive compounds requires special machinery in order to utilize the film in a production environment. Still, another problem is that the prior art anisotropic conductive compounds cannot effectively be utilized with integrated circuits, integrated circuit packages or substrates having adjacent contacts with edge-to-edge spacings less than about 300 μm.

[0008] It is, therefore, an object of the present invention to overcome the above problems and others by providing an improved anisotropic conductive compound and a method of curing thereof. Still other objects will become apparent to those of ordinary skill in the art upon reading and understanding the following detailed description.

SUMMARY OF THE INVENTION

[0009] The invention is a method of forming an electronic assembly comprising (a) providing a first substrate having a plurality of conductive contacts; (b) providing a second substrate having a plurality of conductive contacts; (c) positioning the first and second substrates with their respective conductive contacts in alignment; (d) sandwiching an uncured anisotropic conductive material between the conductive contacts of the first and second substrates, the anisotropic conductive material including electrically conducting material suspended in a binder; (e) heating the anisotropic conductive material to a curing temperature for an interval sufficient to cause the binder to cure to a solid; (f) vibrating the electrically conducting material; and (g) subjecting the electrically conducting material to a static, substantially homogeneous DC magnetic field, wherein the DC magnetic field has a field vector direction that is substantially parallel with the alignment of the conductive contacts of the first and second substrates.

[0010] Step (f) can include vibrating the electrically conducting material utilizing at least one of mechanical vibration and a magnetic field.

[0011] The electrically conducting material can be vibrated at a frequency in the ultrasonic frequency range.

[0012] At least one of step (f) and step (g) can be performed during step (e); step (f) can commence before step (g); and/or step (f) and step (g) can occur at least partially concurrently.

[0013] The invention also a method of forming an electronic assembly comprising (a) sandwiching an uncured anisotropic conductive material between at least one pair of opposed conductive contacts, the anisotropic conductive material including electrically conducting material suspended in a binder; (b) causing the binder to cure to a solid; (c) vibrating the electrically conducting material; and (d) during curing of the binder to a solid, subjecting the electrically conducting material to a static, substantially homogeneous DC magnetic field, wherein the DC magnetic field has a field vector direction that is substantially parallel with the alignment of the pair of conductive contacts.

[0014] Step (c) can include vibrating the electrically conducting material at least one of mechanically and via a magnetic field. Step (c) can be performed during curing of the binder to a solid.

[0015] The invention is also a method of forming an electronic assembly comprising vibrating conductive material or particles of an anisotropic conductive compound or material sandwiched between at least two aligned conductive contacts while the anisotropic conductive compound is curing and subjecting the conductive material to a static, substantially homogeneous DC magnetic field (i) before, (ii) following or (iii) at least partially during the time the conductive material is being vibrated.

[0016] The conductive material or particles can be vibrated at least one of mechanically and via a magnetic field.

BRIEF DESCRIPTION OF THE DRAWINGS

[0017]FIG. 1 is a perspective view of the positioning of an integrated circuit package oil an anisotropic conductive material in accordance with the present invention deposited on a substrate;

[0018]FIG. 2a is a view of the integrated circuit package in spaced relation to the substrate and conductive material taken along section lines II-II in FIG. 1;

[0019]FIG. 2b is a view of the integrated circuit package in contact with the anisotropic conductive material deposited on the substrate taken along section lines II-II in Fig. 1;

[0020]FIG. 3 is a schematic representation of a curing oven having a magnetic field generator therein for curing the anisotropic conductive material sandwiched between the integrated circuit package and the substrate in FIG. 2b;

[0021] FIGS. 4 is a plot of current versus time and field strength versus time for the current through the windings of the magnetic field generator and the magnetic field produced thereby, respectively, in FIG. 3; and

[0022]FIG. 5 is an close-up isolated diagrammatic cross-section of a pair of isolated parallel conductive paths of cured anisotropic conductive material in accordance with the present invention showing the distribution of the electrically conducting material in the binder.

DETAILED DESCRIPTION OF THE INVENTION

[0023] The present invention is an anisotropic conductive material and a method of curing thereof. The invention will first be described in connection with the method of curing the anisotropic conductive material followed by a description of an exemplary anisotropic conductive material that has been found to be particularly suitable for use in forming conductive paths between conductive contacts of an integrated circuit or integrated circuit package and conductive contacts on a substrate that are in alignment with the conductive contacts on the integrated circuit or integrated circuit package while avoiding shorts between adjacent conductive paths. The material is particularly suitable for creating isolated conductive paths between contacts of an integrated circuit and contacts of a substrate having an edge-to-edge spacing less than 250 μm and as small as about 80 μm to 100 μm. An advantage of the present invention is that the method of curing the anisotropic conductive material does not require pressure to be applied between the integrated circuit or integrated circuit package and the substrate. Rather, the weight of the integrated circuit or integrated circuit package acting upon the anisotropic conductive material deposited on the substrate in combination with the method for curing the anisotropic conductive material described hereinafter is sufficient to create conductive paths between contacts of the integrated circuit or integrated circuit package and the contacts on the substrate in alignment therewith while avoiding electrical shorting between adjacent conductive paths.

[0024] Other than in the operating examples, or where otherwise indicated, all numbers expressing quantities of ingredients, reaction conditions and so forth used in the specification and claims are to be understood as being modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that may vary depending upon the desired properties sought to be obtained by the present invention.

[0025] Also, it should be understood that any numerical range recited herein is intended to include all sub-ranges subsumed therein. For example, a range of “1 to 10” is intended to include all sub-ranges between and including the recited minimum value of 1 and the recited maximum value of 10, that is, having a minimum value equal to or greater than 1 and a maximum value of equal to or less than 10. Because the disclosed numerical ranges are continuous, they include every value between the minimum and maximum values. Unless expressly indicated otherwise, the various numerical ranges specified in this application are approximations.

[0026] As used herein, the term “polymer” is meant to encompass oligomers, and includes without limitation both homopolymers and copolymers. As used herein, “(meth)acrylate” and like terms are intended to include both acrylates and methacrylates.

[0027] As used herein the term aryl refers to aromatic groups that include, without limitation, groups such as phenyl, biphenyl, benzyl, xylyl, napthalenyl, anthracenyl and the like, as well as heterocyclic aromatic groups that include, without limitation, pyridinyl, pyrrolyl, furanyl, thiophenyl, and the like.

[0028] With reference to FIG. 1, an integrated circuit package or substrate 2 includes a plurality of closely spaced contacts positioned on or adjacent the edges of package 2. In FIG. 1, package 2 is illustrated as a leadless chip carrier package. However, this is not to be construed as limiting the invention since use of the anisotropic conductive material of the present invention with other surface mount integrated circuit packages, such as ball grid arrays, dual inline or quad packages having gull-wing or j-shaped leads, and quad flat packs having laterally extending leads or any other form of integrated circuit package or substrate having closely spaced leads, is envisioned. In addition, use of the anisotropic conductive material of the present invention with unpackaged integrated circuits for flip-chip mounting thereof is also envisioned.

[0029] As shown in FIG. 1, package 2 is received on a substrate 6 having a plurality of closely spaced contacts 8 disposed in mirror image relation to contacts 4 of package 2. Prior to mounting package 2 on substrate 6, a drop or coating of uncured anisotropic conductive material 10 is deposited on substrate 6 over the plurality of contacts 8.

[0030] With reference to FIGS. 2a and 2 b, and with continuing reference to FIG. 1, next, integrated circuit package 2 is positioned with its contacts 4 in opposition with the contacts 8 of substrate 6. More specifically, each contact 4 of integrated circuit package 2 is positioned in alignment with a corresponding contact 8 of substrate 6. Thereafter, as shown in FIG. 2b, integrated circuit package 2 is moved into contact with anisotropic conductive material 10. In response to this contact, anisotropic conductive material 10 displaces somewhat. However., the viscosity of anisotropic conductive material 10 is such that contacts 4 of integrated circuit package 2 and contacts 8 of substrate 6 are maintained in spaced relation by anisotropic conductive material 10. Importantly, integrated circuit package 2 is moved into contact with anisotropic conductive material 10 in a manner so that contacts 4 of integrated circuit package 2 and contacts 8 of substrate 6 are not in physical contact with each other and the displacement of anisotropic conductive material 10 is due primarily to the weight of integrated circuit package 2. and only slightly due to the force utilized to move integrated circuit package 2 into contact with anisotropic conductive material 10.

[0031] After integrated circuit package 2 is deposited on anisotropic conductive material 10 with each contact 4 in alignment with a corresponding contact 8 of substrate 6, a UV curable adhesive 11 is deposited between substrate 6 and integrated circuit package 2. The UV curable adhesive can be deposited around the perimeter of integrated circuit package 2. However, in practice, it is only necessary to deposit UV curable adhesive 11 on two or more cornets of integrated circuit package 2.

[0032] After UV curable adhesive 11 has been deposited, it is exposed to UV light from one or more light sources L for a sufficient interval to cause UV curable adhesive 11 to commence curing. In addition, if anisotropic conductive material 10 includes a UV curable component, exposure to the UV light from the one or more light sources L also causes this component to commence curing. Optionally, instead of using UV curable adhesive 11, another form of adhesive that can be cured independent of anisotropic conductive material 10 can be utilized. However, UV curable adhesive 11 is preferred since it can be cured without exposing it and anisotropic conductive material 10 to an elevated curing temperature.

[0033] With reference to FIG. 3, and with ongoing reference to all previous Figs., after UV curable adhesive 11 has cured, the entire assembly, including integrated circuit 2, substrate 6 and anisotropic conductive material 10, is positioned in a curing oven 12. In a production environment, curing oven 12 can have a conveyor 14 which extends through curing oven 12 between an inlet 16 and outlet 18 thereof for transporting the assembly therethrough. Alternatively, curing oven 12 can be an enclosure of any suitable shape and size in which the assembly can be positioned.

[0034] Curing oven 12 includes a heating means 20 for heating the atmosphere, e.g., air, inside of curing oven 12 in a manner known in the art. Curing oven 12 also includes a magnetic field generator 22 disposed therein which is coupled to and controlled by an electrical power source 24 disposed external to curing oven 12. Magnetic field generator 22 includes a pair of poles 26 disposed in spaced relation across a gap 28 in which integrated circuit package 2 deposited on anisotropic conductive material 10 received on substrate 6 is positioned in or passes through on conveyor 14. Each pole 26 includes a pole element 30 of ferromagnetic or paramagnetic material having one or more windings 32 of wire or other suitable conductive material formed therearound in a manner known in the art. Windings 32 are electrically insulated from pole elements 30 by a suitable insulator on pole elements 30 and/or a suitable insulator around the wire or other conductive material forming windings 32. Windings 32 of each pole 26 are connected to each other and to electrical power source 24 in a manner whereupon, in response to electrical power source 24 supplying windings 32 with a suitable electrical current, a magnetic field 34 is generated across gap 28.

[0035] Poles 26 are configured so that magnetic field 34 is highly homogeneous, at least where integrated circuit package 2 received on anisotropic conductive material 10 deposited on substrate 6 is positioned in curing oven 12 during curing of anisotropic conductive material 10. Magnetic field 34 preferably has a homogeneity of greater than 98.5%, but can have a homogeneity as low as 95%.

[0036] With reference to FIG. 4, and with continuing reference to all previous Figs., desirably electrical power source 24 initially applies an alternating current signal 36 to windings 32 for a duration between 15 and 30 seconds followed by a direct current signal 38 for the remainder of the curing time of anisotropic conductive material 10. However, this is not to be construed as limiting the invention since the alternating current signal 36 and the direct current signal 38 can be applied to windings 32 concurrently. The amplitude of the alternating current signal 36 can be selected based on the sizes of particles (discussed hereinafter) forming anisotropic conductive material 10. The amplitude of alternating current signal 36 is selected so that magnetic field 34 has an alternating magnetic field strength between 10 and 100 gauss. The value of direct current signal 38 is selected so that magnetic field 34 has a static magnetic field strength between 400 and 1,500 gauss.

[0037] Magnetic field 34 includes the alternating magnetic field produced by magnetic field generator 22 in response to alternating current signal 36 and the static magnetic field produced by magnetic field generator 22 in response to direct current signal 38. It has been observed that alternating current signal 36 operating in the ultrasonic frequency range, namely, between about 20 kHz and about 500 kHz, works best with anisotropic conductive material 10. However, this is not to be construed as limiting the present invention since other frequencies outside of the ultrasonic frequency range can also be utilized.

[0038] At a suitable time, the assembly is positioned in curing oven 12 in the presence of magnetic field 34. Curing oven 12 is heated or preheated to a suitable curing temperature for anisotropic conductive material 10 and the assembly is subjected to this curing temperature for a suitable curing interval while in the presence of magnetic field 34. Because of its nature, the curing temperature and the curing interval of anisotropic conductive material 10 can vary between 70° C. for about 30 minutes to 1 50° C. for about 5- 7 minutes.

[0039] A vibrator 50 (show in phantom) can also be utilized to mechanically vibrate the assembly comprised of anisotropic conductive material 10 sandwiched between integrated circuit package 2 and substrate 6. The amplitude, frequency and duration of this mechanical vibration can be selected based on the size of the particles forming anisotropic conductive material. It is believed that vibrating the assembly at a frequency in the ultrasonic frequency range for between 15 and 30 seconds will work best with anisotropic conductive material 10. However, this is not to be construed as limiting the invention.

[0040] Vibrator 50 can mechanically vibrate the assembly while it is in the presence of the curing temperature in curing oven 12. Before, concurrent with, partially concurrent with or following mechanical vibration thereof, the assembly, especially the particles of the anisotropic conductive material, can be subjected to magnetic field 34. It is envisioned that magnetic field 34 can include any suitable combination of the alternating magnetic field and the static magnetic field when magnetic field 34 is used before, concurrent with, partially concurrent with or following mechanical vibration of the assembly. For example, magnetic field 34 can include (i) the alternating magnetic field followed by the static magnetic field, or vice versa, (ii) the alternating magnetic field applied concurrent with the static magnetic field. or (iii) the alternating magnetic field applied partially concurrent with the static magnetic field, where either the alternating magnetic field or the static magnetic field is initiated first. The foregoing listing of combinations of alternating magnetic field and static magnetic field used before, concurrent with, partially concurrent with or following mechanical vibration of the assembly, however, is not to be construed as limiting the invention.

[0041] If it is determined that mechanically vibrating the assembly obviates the need for the alternating magnetic field, magnetic field 34 can exclude the alternating magnetic field and only apply the static magnetic field to the assembly before, concurrent with, partially concurrent with or following mechanical vibration of the assembly.

[0042] With reference to FIG. 5, and with continuing reference to all previous Figs., once cured to a solid, anisotropic conductive material 10 forms a conductive path between each contact 4 of integrated circuit package 2 and a corresponding contact 8 of substrate 6 in alignment therewith. It has been observed that cured anisotropic conductive material 10 can form electrically conductive, but isolated parallel conductive paths 48 between adjacent pairs of aligned contacts having an edge-to-edge spacing S as close as 80 μm. This is a vast improvement over prior art anisotropic conductive materials which, when cured, have difficulty maintaining electrical isolation between adjacent conductive paths between adjacent pairs of aligned contacts having an edge-to-edge spacing below 250 m.

[0043] As shown in FIG. 1, anisotropic conductive material 10 includes an electrically conducting material 40 suspended in a binder 42. Electrically conducting material 40 includes one or more types of particles coated with a noble metal such as gold or silver. The particles forming electrically conducting material 40 can include one or more of the following: solid nickel coated spheres, solid nickel flakes, solid carbon/graphite spheres, solid glass spheres, solid mica particles or flakes and hollow glass spheres. As used herein, the terms sphere or spheres generally means that the particles are ball-shaped, egg-shaped or minor variations of ball-shaped and egg-shaped.

[0044] The solid carbon/graphite spheres, the solid glass spheres, the solid mica particles or flakes and the hollow glass spheres each include a coating of nickel between the outside surface of the sphere and the coating of noble metal. The coating of nickel on these otherwise non-magnetic materials renders them susceptible to the influence of magnetic field 34.

[0045] Each particle along with the one or more coatings thereon has a maximum dimension less than 100 μm, preferably less than 80 μm and more preferably between 10 μm and 25 μm. As used herein, the term “maximum dimension” means the largest dimension of the particle measured in any direction. For example, if a particle is a sphere, the maximum dimension is the outside diameter of the noble metal deposited on the sphere. If the particle is a flake having an irregular shape, the maximum dimension is the dimension between the two points of the noble metal deposited over the particle that are farthest apart.

[0046] It has been observed that particles having an average maximum dimension between 10 μm and 25 μm enables the formation of parallel isolated conductive paths between adjacent pairs of aligned contacts having an edge-to-edge spacing as close as 80 μm. Obviously, a plurality of particles having this average maximum dimension will have some particles having less than 10 μm, e.g., 5 μm, and some particles having a maximum dimension greater than 25 μm. To this end, it has been observed that in a population of particles forming electrically conducting material 40 with an average maximum dimension between 10 μm and 25 μm, some of the particles can have a maximum dimension as small as 5 μm.

[0047] A first embodiment anisotropic conductive material 10 includes binder 42 formed from the reaction product of between 82% and 91% by weight of a compound and no more than about 6% by weight of a catalyst. The compound includes about one-third by weight of each of an aromatic epoxy resin, a dimer fatty acid diglycidyl ester and an oxirane. Any suitable aromatic epoxy resin may be used in the compound. Suitable aromatic epoxy resins include, but are not limited to diglycidyl ethers of bisphenol-A and bisphenol-F and other such resins, such as those available from EPON Resins from Resolution Performance Products, Houston, Texas. Any suitable dimer fatty acid diglycidyl ester may be used in the compound. Suitable dimer fatty acid diglycidyl esters include those of the formula:

[0048] where R is C₁-C₂₀ alkylene, arylene or alkarylene.

[0049] Any suitable oxirane may be used in the compound. Suitable oxiranes include those of the formula:

[0050] where R² is linear or branched C₁-C₂₀, alkyl, aryl, alkaryl, or is derived from a poly ether of the formula:

[0051] where R³ is a linear or branched C₁-C₁₂ alkylene and R⁴ is a linear or branched C₁-C₂₀ alkyl, aryl or alkaryl group, and “n” is an integer from 1 to 100. In an embodiment of the invention, the oxirane is (butoxy methyl)—butyl glycidyl ether. In one non-limiting embodiment. the aromatic epoxy resin is the reaction product of about one-half by weight of each of bisphenol-A and epichlorohydrin. In one non-limiting embodiment, the catalyst includes a quaternary cyanyl R-substituted amine. The R group in the quaternary cyanyl R-substituted amine may be a C¹-C₂₀ linear or branched alkyl, aryl or aralkyl group. In this first embodiment anisotropic conductive material 10, electrically conducting material 40 includes between 2.5% and 7% by weight of solid nickel spheres coated with silver and between 2.5% and 7% by weight of solid nickel flakes coated with silver.

[0052] A second embodiment anisotropic conductive material 10 includes the same electrically conducting material as the first embodiment anisotropic conductive material 10 and a binder similar to binder 42 in the first embodiment anisotropic conductive material 10 described above except that the binder in this second embodiment includes about 10% by weight of a UV curable modifier which replaces a corresponding weight percentage of the compound. More specifically, binder 42 in the second embodiment anisotropic conductive material 10 is formed from the reaction product of the UV curable modifier, the catalyst and the above described compound. The UV modifier can be UV curable adhesive 11 of the type commonly used in the art to attach integrated circuit packages to substrates. One exemplary UV curable modifier is formed from the reaction product of between 8% and 12% by weight of a (meth)acrylate ester, between 76% and 84% by weight of (meth)acrylated urethane and between 4% and 5% by weight of a hydroxy alkyl aryl ketone.

[0053] Any suitable (meth)acrylate ester may be used in the UV curable modifier. Suitable (meth)acrylate esters include those of the formula of:

[0054] where R⁵ is H or methyl and R⁶ is a linear, branched or cyclic C¹-C₂₀ alkyl, aryl, alkaryl or aralkyl group. In an embodiment of the UV curable modifier, the (meth)acrylate ester is isobutyl (meth)acrylate. Any suitable hydroxy alkyl aryl ketone may be used in the UV curable modifier. Suitable hydroxy alkyl aryl ketones include those of the formula:

[0055] Where R⁷ is a linear, branched or cyclic C₂-C₂₀ alkyl group containing at least one hydroxyl group and R⁸ is a C₆-C₂₀ aryl, alkaryl or aralkyl group. In an embodiment of the UV curable modifier, the hydroxy alkyl aryl ketone is 1-hydroxy cycohexyl phenyl ketone.

[0056] A third embodiment anisotropic conductive material 10 includes binder 42 formed from the reaction product of between 8% and 12% by weight of the compound described above, between 71% and 79% of a phenolic resin, no more than about 6% by weight of a catalyst, such as a quaternary cyanyl R-substituted amine, and no more than about 12% by weight of the UV modifier system. Any suitable phenolic resin may be used in the present invention. Suitable phenolic resins include, but are not limited to, novalac resins and revol resins. In an embodiment of the invention, the phenolic resin is a novalac resin formed as the reaction product of formaldehyde and one or more of phenol, cresol, bisphenol-A and bisphenol-F. The quaternary cyanyl R-substituted amine is as described above. This binder 42 is mixed with about 14% by weight of an electrically conducting material 40 to form the third embodiment anisotropic conductive material 10. In this embodiment, electrically conducting material 40 is solid nickel spheres coated with gold.

[0057] A fourth embodiment anisotropic conductive material 10 includes binder 42 formed from the reaction product of between 71% and 79% by weight of phenolic resin, as described above, 8% to 12% by weight of a thermally polymerized aromatic epoxy resin and no more than about 6% by weight of a catalyst, such as quaternary cyanyl R-substituted amine as described above. The electrically conducting material 40 added to this fourth embodiment binder 42 to form anisotropic conductive material 10 includes about 10% by weight of solid carbon/graphite spheres having a coating of gold over a coating of nickel and about 4% by weight of solid glass spheres having a coating of gold over a coating of nickel.

[0058] A fifth embodiment anisotropic conductive material 10 includes binder 42 formed from the reaction product of between 71% and 79% by weight of a phenolic resin, as described above, 8% to 12% by weight of a phenoxy modified epoxy novalac resin and no more than about 6% by weight of a catalyst, such as quaternary cyanyl R-substituted amine as described above. The electrically conducting material 40 of the fifth embodiment anisotropic conductive material 10 includes about 10% by weight of solid carbon/graphite spheres having a coating of gold over a coating of nickel and about 4% by weight of solid glass spheres having a coating of gold over a coating of nickel.

[0059] When the particles comprising electrically conducting material 40 of the first through fifth embodiments of anisotropic conductive material 10 have an average maximum dimension between 10 μm and 25 μm and when each of these anisotropic conductive materials 10 are cured in the above described manner, adjacent parallel isolated conductive paths having an edge-to-edge spacing as close as 80 μm were observed in cross sections of the cured anisotropic conductive material 10. The isolation of these adjacent parallel isolating conductive paths was confirmed by electrical measurement thereof.

[0060] The first through fifth embodiments of anisotropic conductive material 10 were utilized to attach 20 pin integrated circuits to substrates and to electrically connect each contact of the integrated circuit to a corresponding contact of the substrate to which the integrated circuit was attached. The contact resistance between one or more contacts of each integrated circuit and the corresponding embodiment of anisotropic conductive material 10 were measured and the following results were observed. The first through third embodiments of anisotropic conductive material 10 exhibited a higher contact resistance than the fourth and fifth embodiments of anisotropic conductive material 10. In addition, the first through third embodiments of anisotropic conductive material exhibited a contact resistance that varied as much as one order of magnitude greater than the contact resistance variance of the fourth and fifth embodiments of anisotropic conductive material 10. More specifically, the contact resistance of the first through third embodiments of anisotropic conductive material 10 varied Up to 20%. In contrast. the contact resistance of the fourth and fifth embodiments of anisotropic conductive material 10 varied between 2% and 4%.

[0061] Moreover, the stability of the contact resistance of the first through third embodiments of anisotropic conductive material 10 increased or decreased by as much as 60% when exposed to 95% relative humidity at 40° C. for 1,000 hours. Furthermore, when the first through third embodiments of anisotropic conductive material 10 were exposed to 60° C. for 1,000 hours, the contact resistance increased or decreased by as much as 15%. Lastly. when the first through third embodiments of anisotropic conductive material 10 were exposed to a temperature of −40° C. for 1,000 hours, the contact resistance increased or decreased by as much as 20%.

[0062] In contrast, the contact resistance of the fourth and fifth embodiments of anisotropic conductive material 10 increased or decreased by only about 7% when exposed to 95% relative humidity at 40° C. for 1,000 hours. Moreover, when the fourth and fifth embodiments of anisotropic conductive material 10 were exposed to a temperature of 60° C. for 1,000 hours, the contact resistance of each contact increased or decreased only about 5%. Lastly, when the fourth and fifth embodiments of anisotropic conductive material 10 were exposed to a temperature of −40° C. for 1,000 hours, the contact resistance of each contact increased or decreased only about 5%.

[0063] The foregoing embodiments of anisotropic conductive material 10 have a viscosity between 30,000 centi-poise and 45,000 centi-poise at 25° C. and a viscosity of less than 50 centipoise between 75° C. and 150° C. This drastic change in viscosity in combination with the exposure of anisotropic conductive material 10 to a suitable curing temperature in the presence of magnetic field 34 enables the electrically conducting material 40 suspended in binder 42 to align under the influence of magnetic field 34 to form adjacent, but electrically isolated, parallel conductive paths between adjacent pairs of aligned contacts having an edge-to-edge spacing as close as 80 μm.

[0064] It is believed that electrically conducting material 40 formed from solid mica particles or flakes and/or hollow glass spheres having a coating of noble metal, such as gold or silver, over a coating of nickel will reduce the edge-to-edge spacing of adjacent parallel isolated conductive paths that can be realized over the edge-to-edge spacing realized utilizing similarly sized solid nickel spheres coated with a coating of noble metal, solid carbon/graphite spheres having a coating of noble metal over a coating of nickel and/or solid glass spheres having a coating of noble metal over a coating of nickel. To this end, it is believed that the lower weight of the solid mica particles or flakes and/or the hollow glass spheres enables them to move more readily under the influence of magnetic field 34 before binder 42 hardens sufficiently to prevent their movement under the influence of magnetic field 34.

[0065] Obviously, smaller particle sizes forming electrically conducting material 40 of anisotropic conductive material 10 enables conductive paths to be formed between adjacent pairs of aligned contacts having a closer edge-to-edge spacing than larger particles. Thus, increasing and deceasing the average maximum dimension of the particles forming electrically conducting material 40 of anisotropic conductive material 10, increases and decreases the edge-to-edge spacing of adjacent pairs of aligned contacts that can be electrically connected by adjacent conductive paths without experiencing shorting between the adjacent conductive paths.

[0066] The present invention has been described with reference to the preferred embodiments. Obvious modifications and alterations will occur to others upon reading and understanding the preceding detailed description. It is intended that the invention be construed as including all such modifications and alterations insofar as they come within the scope of the appended claims or the equivalents thereof. 

The invention is claimed to be:
 1. A method of forming an electronic assembly comprising: (a) providing a first substrate having a plurality of conductive contacts; (b) providing a second substrate having a plurality of conductive contacts; (c) positioning the first and second substrates with their respective conductive contacts in alignment; (d) sandwiching an uncured anisotropic conductive material between the conductive contacts of the first and second substrates, the anisotropic conductive material including electrically conducting material suspended in a binder; (e) heating the anisotropic conductive material to a curing temperature for an interval sufficient to cause the binder to cure to a solid; (f) vibrating the electrically conducting material; and (g) subjecting the electrically conducting material to a static, substantially homogeneous DC magnetic field, wherein the DC magnetic field has a field vector direction that is substantially parallel with the alignment of the conductive contacts of the first and second substrates.
 2. The method of claim 1, wherein step (f) includes vibrating the electrically conducting material utilizing at least one of mechanical vibration and a magnetic field.
 3. The method of claim 1, wherein, in step (f), the electrically conducting material is vibrated at a frequency in the ultrasonic frequency range.
 4. The method of claim 1, wherein at least one of step (f) and step (g) is performed during step (e).
 5. The method of claim 1, wherein at least one of the first and second substrates is an electronic component.
 6. The method of claim 1, wherein step (f) occurs before step (g), or vice versa.
 7. The method of claim 1, wherein step (f) and step (g) occur at least partially concurrently.
 8. A method of forming an electronic assembly comprising: (a) sandwiching an uncured anisotropic conductive material between at least one pair of aligned conductive contacts, the anisotropic conductive material including electrically conducting material suspended in a binder; (b) causing the binder to cure to a solid; (c) vibrating the electrically conducting material; and (d) during curing of the binder to a solid, subjecting the electrically conducting material to a static, substantially homogeneous DC magnetic field, wherein the DC magnetic field has a field vector direction that is substantially parallel with the alignment of the pair of conductive contacts.
 9. The method of claim 8, wherein step (c) includes vibrating the electrically conducting material at least one of mechanically and via a magnetic field.
 10. The method of claim 8, wherein at least one of step (c) and step (d) is performed during curing of the binder to a solid.
 11. A method of forming an electronic assembly comprising vibrating conductive material or particles of an anisotropic conductive compound or material sandwiched between at least two aligned conductive contacts while the anisotropic conductive compound is curing and subjecting the conductive material to a static, substantially homogeneous DC magnetic field (i) before, (ii) following or (iii) at least partially during the time the conductive material is being vibrated.
 12. The method of claim 1, wherein the conductive material or particles are vibrated at least one of mechanically and via a magnetic field. 